Optical waveguide with layered core and methods of manufacture thereof

ABSTRACT

A semiconductor waveguide is disclosed which includes a substrate coated with a cladding. A core is embedded in the cladding. The core includes a plurality of discreet stacked layers of core material surrounded by cladding material. The cladding and core layers each include silica and silicon nitride with the core layers having a higher nitrogen content than the cladding material. The core is fabricated by carefully manipulating the process parameters of a PECVD process.

This is a divisional of application Ser. No. 10/136,729 filed on May 1, 2002, now U.S. Pat. No. 6,670,210.

TECHNICAL FIELD

Semiconductor opto-electronic devices including semiconductor optical waveguides and methods of manufacture thereof are disclosed.

BACKGROUND OF THE RELATED ART

There is a wide-ranging demand for increased communications capabilities, including more channels and greater bandwidth per channel. The needs range from long distance applications such as telecommunications between two cities to extremely short range applications such as the data-communications between two functional blocks (fubs) in a semiconductor circuit with spacing on the order of a hundred microns.

Optical fibers can carry information encoded as optical pulses over long distances. The advantages of optical media include vastly increased data rates, lower transmission losses, lower basic cost of materials, smaller cable sizes, and almost complete immunity from stray electrical fields. Other applications for optical fibers include guiding light to awkward places (e.g., surgical applications), image guiding for remote viewing, and various sensing applications.

Optical fibers or waveguides provide an economical and higher bandwidth alternative to electrical conductors for communications. A typical optical fiber includes a silica core, a silica cladding, and a protective coating. The index of refraction of the core is higher than the index of refraction of the cladding to promote internal reflection of light propagating down the silica core.

Waveguides have been developed comprising a mixture of silica (SiO₂) and silicon nitride (Si₃N₄), often referred to as SiON. The indexes of refraction of the core and cladding can be controlled by controlling the nitrogen content. That is, the nitrogen content of the core will be higher than that of the cladding to give the core a suitably higher index of refraction than the cladding.

However, the differences in the index of refraction of the core and cladding also result in birefringence, or the separation of the light pulse or ray into two unequally refracted pulses or rays. As a result, part of the light transmission is lost. For fiber optic communication systems where long range fiber optic communication is utilized, there is a need for optical and electro-optic devices that are substantially free from birefringence.

In general, birefringence is the difference between a refractive index n_(TM) for the TM mode having a field component perpendicular to the substrate and a refractive index n_(TE) for the TE mode having a field component parallel to the substrate, or, the birefringence equals n_(TM)-n_(TE).

The majority of fiber optic telecommunications systems use standard single-mode silica fiber that does not preserve the polarization of the transmitted light. For such systems, the polarization state of the light signal in the optical fiber at any point and at any time is unknown and subject to variation over time and distance as a result of environmental and other changes that occur along the transmission path of the signal. If devices placed at any point in the fiber transmission path or at its end have response characteristics that depend on the polarization state of the light (i.e., polarization dependence), the signal may be degraded or lost altogether.

As integrated optical and electro-optical devices are employed in fiber optic systems for which the polarization state of the light signal is unknown, a need arises to circumvent or minimize the consequences of the polarization dependence and birefringence of these devices.

The most popular approach for reducing the effects of birefringence has been to introduce additional components to control the state of polarization of the light signal before its introduction to the polarization-sensitive device.

A more satisfactory approach would be to provide a waveguide device with a small polarization dependence and birefringence thereby causing only negligible transmission degradation.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a sectional view of a fiber optic waveguide made in accordance with this disclosure;

FIG. 2 is a sectional of a substrate, coated with a cladding layer and a plurality of alternating core and cladding layers to form a stacked core in accordance with this disclosure after the core has been etched;

FIG. 3 is a sectional view of a waveguide manufactured in accordance with this disclosure after a cladding layer is been deposited on top of the stacked core and after the structure has been annealed to cause the stacked layers of the core to interdiffuse thereby reducing scattering caused by edge wall index perturbation;

FIG. 4 is a phase diagram for a binary SiO₂—Si₃N₄ system illustrated in the use of a lower process temperature for a PECVD process for generating the stacked layer core structure illustrated in FIGS. 1-3;

FIG. 5 illustrates, graphically, the tensile and compressive forces for a binary SiO₂—Si₃N₄ system; and

FIG. 6 illustrates, graphically, the index of refraction for various SiO₂—Si₃N₄ binary systems.

DETAILED DESCRIPTION OF THE PRESENTLY PREFERRED EMBODIMENTS

To provide an optical waveguide and other opto-electronic devices with reduced birefringence and reduced polarization dependence, waveguide and devices are made from binary systems of silica and silicon nitride. Using a plasma enhanced chemical vapor deposition (PECVD) process, a waveguide 10 having the structure illustrated in FIG. 1 is fabricated. The waveguide 10 includes a substrate 11 and a cladding 12. Embedded in the cladding 12 is a series of discreet layers 13 that form a core 14. Both the cladding 12 and the layers 13 of the core 14 comprise both silica and silicon nitride, or SiON. However, the cladding layer 12 has a lower nitrogen content that the discreet stacked layers 13 of the core 14. In the alternative, it is noted that the cladding 12 has a higher oxygen content than the discreet stacked layers 13 of the core 14.

To fabricate the waveguide 10 of FIG. 1, a cladding layer 12 is deposited on a substrate 11, preferably using a PECVD process using silane, nitrous oxide and either ammonia or nitrogen as precursor gases fed to a chamber. To maintain an appropriate nitrogen content in the cladding layer 12, a predetermined flow rate of the ammonia or nitrogen is utilized. Then, to deposit an initial core layer 13 a (see FIG. 2), the flow rate of the nitrogen or ammonia is increased to generate a core layer 13 a. After a sufficient first core layer 13 a is deposited, the nitrogen or ammonia flow rate is reduced to provide a cladding layer 12 a disposed on top of the core layer 13 a. Then, the nitrogen or ammonia flow rate is again increased to produce the second core layer 13 b. This sequence is repeated to form the layers 12 b, 13 c, 12 c and 13 d. Then, using a masking layer, the core 14 is etched. Then, as shown in FIG. 3, additional cladding material is deposited on top of the core 14. The materials for the cladding 12 and core layers 13 are deposited at moderate temperatures ranging from about 450° C. to about 800° C. or possibly higher, depending upon the reactor used.

The entire structure is then annealed to provide the interlayer diffusion illustrated in FIG. 3. The temperature of the anneal process will typically range from about 1000° C. to about 1300° C., more preferably at the lower end of this range, from about 1000° C. to about 1100° C. It will be noted that only small differences in the nitrogen content (or the oxygen content) the cladding 12 and core layers 13 are required in order to generate a sufficient index of a refraction. Specifically, the relatively steep slope of the refractive index illustrated in FIG. 6 for a SiO₂—Si₃N₄ system establishes this proposition.

Turning to FIG. 4, it is evident that a single process temperature can be utilized for the deposition of the silica rich cladding layer 12 and the silicon nitride rich core layers 13. Specifically, points 15 and 16 of FIG. 4 fall outside of the region 17 of reported crystallization in the silicon nitride. Further, by maintaining the constant process temperature T_(p) during the cladding 12 and core layer 13 depositions, and the subsequent annealing, the flow temperatures of the cladding 12 and core layers 13 match which will reduce sidewall roughness of the core 14. Specifically, the core layers 13 and cladding 12 will soften and flow at the same temperature, and as a result, intermixing and interdiffusion will occur.

In contrast, when strong intermixing and interdiffusion does not occur, there will be a natural surface tension forming between two crystallized materials. Therefore, the simultaneous flow will induce a straightening of the interface between the two materials thereby reducing sidewall roughness. By maintaining the process temperature constant during the deposition of the cladding 12 and core layers 13, surface tension between the two materials is reduced thereby reducing the stress-induced birefringence.

Further, as illustrated in FIG. 5, moderate stress will be indicated from two similar compositions used for the cladding 12 and core layers 13. However, the tensile stress illustrated in FIG. 5 can be used to compensate for polarization dependence. Specifically, the layering birefringence caused by the stacked layers 13 can be used to compensate for stressed induced birefringence if the composition of the cladding 12 and core layers 13 are appropriately chosen using the data in FIG. 5. FIG. 6 illustrates that two materials of such a similar composition still exhibit suitable refractive index differences and the relatively small refractive index differences combined with the induce stress results in polarization dependence compensation.

The differences in nitrogen content and oxygen content of the cladding 12 and core layers 13 will depend upon the surface area of the structure. Using the fraction x for SiO₂ content in the cladding and y for Si₃N₄ content in the cladding where x+y=1, when the surface area of the cladding 12 is about 1×1 μm, the Si₃N₄ content of the core layers 13 should exceed the Si₃N₄ content of the cladding 12 by 0.1 to about 0.2. In contrast, when the surface area of the cladding is about 3×3 μm, the Si₃N₄ content of the core layers 13 should exceed the Si₃N₄ content of the cladding 12 by 0.03 to 0.05. When the surface area of the cladding 12 is about 6×6 μm, the Si₃N₄ content of the layers 13 of the core 14 should exceed the Si₃N₄ content of the cladding 12 by about 0.01 to about 0.03. In other words, the larger the surface area of the cladding 12, a lower difference in Si₃N₄ content between the cladding 12 and core layers 13 is required. The same is also true for SiO₂ content.

In the foregoing detailed description, the disclosed structures and methods have been described with reference exemplary embodiments. It will, however, be evident that various modifications and changes may be made thereto without departing from the broader spirit and scope of this disclosure. The above specification and figures are to be regarded as illustrative, rather than restrictive. Particular materials selected herein can easily be substituted for other materials that will be apparent to those skilled in the art and would nevertheless remain equivalent embodiments of the disclosed structures and methods. 

1. A semiconductor waveguide comprising: a substrate, the substrate coated with a cladding, a core embedded in the cladding, the core comprising a plurality of discreet stacked layers of core material surrounded by cladding, the cladding comprising SiO₂ and Si₃N₄, the layers of the core material comprising SiO₂ and Si₃N₄, the layers of the core having a nitrogen content that is greater than a nitrogen content of the cladding, wherein a stress is present at interfaces between each layer of core material and surrounding cladding to create a stress polarization effect at each layer, the combined stress effects of the layers of core material acting to at least partially cancel each other out to reduce polarization dependence of the waveguide.
 2. The waveguide of claim 1 wherein the nitrogen content of the layers of the core exceed the nitrogen content of the cladding by about 0.1 to about 0.2 when a surface area of the cladding is about 1×1 μm.
 3. The waveguide of claim 1 wherein the nitrogen content of the layers of the core exceed the nitrogen content of the cladding by about 0.03 to about 0.05 when a surface area of the cladding is about 3×3 μm.
 4. The waveguide of claim 1 wherein the nitrogen content of the layers of the core exceed the nitrogen content of the cladding by about 0.01 to about 0.03 when a surface area of the cladding is about 6×6 μm.
 5. The waveguide of claim 1 wherein a mole fraction of Si₃N₄ in the layers of the core exceed a mole fraction of Si₃N₄ in the cladding by an amount ranging from about 0.1 to about 0.2.
 6. The waveguide of claim 5 wherein a surface area of the cladding is about 1 μm×1 μm.
 7. The waveguide of claim 1 to produce alternating layers of cladding material and core material and wherein a mole fraction of Si₃N₄ in the layers of the core exceed a mole fraction of Si₃N₄ in the cladding by an amount ranging from about 0.1 to about 0.2.
 8. The waveguide of claim 1 wherein a mole fraction of Si₃N₄ in the layers of the core exceed a mole fraction of Si₃N₄ in the cladding by an amount ranging from about 0.03 to about 0.05.
 9. The waveguide of claim 8 wherein a surface area of the cladding is about 3 μm×3 μm.
 10. The waveguide of claim 1 wherein a mole fraction of Si₃N₄ in the layers of the core exceed a mole fraction of Si₃N₄ in the cladding by an amount ranging from about 0.03 to about 0.05 and a surface area of the cladding is about 3 μm×3 μm.
 11. The waveguide of claim 1 wherein a mole fraction of Si₃N₄ in the layers of the core exceeds a mole fraction of Si₃N₄ in the cladding by an amount ranging from about 0.01 to about 0.03.
 12. The waveguide of claim 8 wherein a surface area of the cladding is about 6 μm by 6 μm.
 13. The waveguide of claim 1 wherein a mole fraction of Si₃N₄ in the layers of the core exceeds a mole fraction of Si₃N₄ in the cladding by an amount ranging from about 0.01 to about 0.03 and a surface area of the cladding is about 6 μm by 6 μm.
 14. The waveguide of claim 7 wherein a stress is present at interfaces between each layer of core material and surrounding cladding to create a stress polarization effect at each layer, the combined stress effects of the layers of core material acting to at least partially cancel each other out to reduce polarization dependence of the waveguide.
 15. The waveguide of claim 10 wherein a stress is present at interfaces between each layer of core material and surrounding cladding to create a stress polarization effect at each layer, the combined stress effects of the layers of core material acting to at least partially cancel each other out to reduce polarization dependence of the waveguide.
 16. The waveguide of claim 13 wherein a stress is present at interfaces between each layer of core material and surrounding cladding to create a stress polarization effect at each layer, the combined stress effects of the layers of core material acting to at least partially cancel each other out to reduce polarization dependence of the waveguide. 